作者：Kuo Lin,Zhongjie Shen,Qinfeng Liang,Jianliang Xu,Haifeng Liu

作者單位：Shanghai Engineering Research Center of Coal Gasification, East China University of Science and TechnologyInstitute of Clean Coal Technology, East China University of Science and Technology

刊名：Chinese Journal of Chemical Engineering

ISSN：1004-9541

出版年：2022-07-15

卷：47

期：7

起頁：271-281

止頁：

分類號：TQ545;TQ175.7

語種：英文

關鍵詞：

內容簡介

The service life of refractory brick in the slag tapping hole of the entrained flow gasifier was significantly lower than that in other locations. It was critically important to study the corrosion mechanism of refractory brick in the slag tapping hole for guiding industrial production. Considering the complex flow field in the slag tapping hole, the influence of gas velocity and temperature fluctuation on the service life of refractory brick was investigated in this study. The results showed that the slag flow characteristics periodically changed with the gas temperature and velocity fluctuations. The brick corrosion rate increased with the decrease of fluctuation frequency. Compared with the gas-phase velocity fluctuation, the gasphase temperature fluctuation had a more significant influence on the brick corrosion rate. When the fluctuation frequency was 0.01 Hz and the gas temperature fluctuation amplitude was 200 K, the corrosion rate of refractory bricks increased by 25%. It could be concluded that the fluctuation of gas-phase temperature was the main cause for the low service life of refractory bricks in the tapping hole.