丹東播磨耐火材料有限公司

浸漬管

項目/Item鎂鉻磚Magnesite-chromebrick澆注料HighaluminacastablerefractoryMgO,%≥70-Al2O3,%-≥70Cr2O3,%≥12-氣孔率/Apparentporosity,%≤18-體密/Bulkdensity,g/cm3≥3.00≥2.70耐壓/Coldcrushingstrength,MPa≥

2024-04-07 電議/噸

浸漬管噴補料

項目/ItemMG-90MgO,%≥60CaO,%≥15抗折強度/Breakingstrength(1500℃×3H),MPa≥1體積密度/Bulkdensity(110℃×24H),g/cm3≥2.0使用溫度/Usagetemperature,℃1750

2024-04-07 電議/噸

高爐出鐵溝澆注料

項目/ItemAT-ZAT-TAl2O3,%≥50≥60SiC,%≥25≥15C,%≥1≥1.5體密/Bulkdensity,g/cm3110℃×24H≥2.7≥2.71500℃×3H≥2.5≥2.5抗折/Bendingstrength,MPa110℃×24H≥25≥251500℃&tim

2024-04-07 電議/噸

鎂質(zhì)火泥

項目/ItemMG-90MgO,%≥80SiO 2,%≤6粒度/Granularityneed(-0.074mm),%≥60

2024-04-07 電議/噸

電爐爐蓋、精煉爐蓋

牌號BrandBM-ABM-ACBM-AMC化學成分/%,≥ChemicalcompositionAl2O3858580Cr2O322體積密度/g﹒cm-3,≥Bulkdensity110℃2.82.82.8耐壓強度/MPa,≥Crushingstrength110℃3030301500℃606060燒后線變化/%Firinglinearchange1500℃±0.

2024-04-07 電議/噸

中間包用耐火材料

Productname產(chǎn)品名稱穩(wěn)流器Impactpot沖擊板Impact擋渣墻Weir澆注料Castable中間包涂料Tundishsmearingmixes中間包干式料DrymixesforTundish中間包包蓋CoverfortundishChemicalPropertiesWeight化學成分（%）MgO≥5808080Al2O3≥70705070Bulkdennity體積密度

2024-04-07 電議/噸

鋼包用鎂碳磚、鎂鋁碳磚、鋁

（1）鋼包用鎂碳磚MagnesiaCarbonBrickforSteelLadle 項目/ItemMC-4MC-8MC-10MC-14MgO,%≥86≥80≥78≥74C,%≥4≥8≥10≥14氣孔率/Apparentporosity,%≤6.0≤6.0≤4.0≤4.0體密/Bulkdensity,g/cm­

2024-04-07 電議/噸

透氣磚

項目/ItemT-80T-85Z-80ZB-85Al2O3,%≥80≥85≥80≥85Al2O3+MgO+Cr2O3,%≥92≥92≥92≥92氣孔率/Apparentporosity,%≤20≤20≤20≤19耐壓強度/Coldcrushingstrength,MPa--85≥45

2024-04-07 電議/支

水口

項目/ItemSK-85SKG-80Al2O3,%≥85≥80C,%≥5≥5氣孔率/Apparentporosity,%≤10≤13體密/Bulkdensity,g/cm3≥3.05≥3.0耐壓強度/Coldcrushingstrength,MPa≥40≥40

2024-04-07 電議/支

滑板

項目/ItemHB-65HB-70HB-75HBLT-65Al2O3,%≥65≥70≥75≥65C,%≥6≥6≥4≥6氣孔率/Apparentporosity,%≤13≤13≤10≤13體密/Bulkdensity,g/cm3≥2.75≥2.85≥3.00≥2.75耐壓/Coldcrushingstr

2024-04-07 電議/支

鋼包引流砂

項目/ItemYL-SYL-CSiO2,%75-9015-35Cr2O3,%1-530-45Al2O3,%5-1010-15Fe2O3,%≤2≤2MgO,%1-55-10粒度/Granularity,mm0-20.15-1自開率,sinceopeningrate%≥98≥98

2024-04-07 電議/噸

剛玉澆注料

項目/ItemAM-80AM-85Al2O3,%≥80≥85氣孔率/Apparentporosity,%≤18≤18耐壓強度/Coldcrushingstrength(110℃×24H),MPa≥35≥35耐壓強度/Coldcrushingstrength(1500℃×3H),MPa≥60≥60線變化率/Linearchang

2024-04-07 電議/噸

鋼包預制塊

項目/ItemYZ-1YZ-2Al2O3,%≥90≥80氣孔率/Apparentporosity,%≤18≤22體積密度/Bulkdensity,g/cm3≥3.00≥2.85耐壓強度/Coldcrushingstrength,(110℃×24H)MPa≥55≥40抗折強度/Bendingstrength,(110℃×24H

2024-04-07 電議/噸

微納米保溫材料

牌號Brand體積密度VolumeDensity/g.cm-3使用溫度OperatingTemperature/℃ 導熱系數(shù)ThermalConductivity/w(m.k)-1耐壓強度Compressivestrength/MPa線變化率/Linearchangerate(1600℃),%350℃1000℃110℃/24h1650℃/24hBWJ-11.5~1.716000.200.

2024-04-07 電議/噸

鋼包澆注料

項目/ItemAM-J1AM-J2AM-J3AM-J4Al2O3+MgO,%≥80≥85≥90≥75體密/Bulkdensity(110℃×24H),g/cm3≥2.6≥2.7≥2.85≥2.2耐壓/Compressivestrength(1500℃×3H),MPa≥30≥40≥50≥40抗折/Ben

2024-04-07 電議/噸

包沿澆筑料

項目/ItemAJ-70AM-85Al2O3,%≥75-MgO,%-≥70氣孔率/Apparentporosity,%≤20≤25耐壓強度/Coldcrushingstrength(110℃×24H),MPa≥30≥30耐壓強度/Coldcrushingstrength(1500℃×3H),MPa≥60≥40線變化率/Line

2024-04-07 電議/噸

噴補料

項目/ItemMZ-80DMC-5DMC-10DMgO,%≥80≥60≥65SiO2,%≤6.0≤6.0≤6.0CaO,%≤3.0≥5.0≥10體密/Bulkdensity,g/cm­3110℃×24H≥2.0≥2.0≥2.01500℃×3H≥2.1≥2.1≥2.1抗折/ben

2024-04-07 電議/噸

出鋼口

2024-04-07 電議/支

電爐用鎂碳磚

項目/ItemMC-10MC-12MC-14MC-16MC-14 使用部位/Part出鋼槽/出鋼口Laundertaphole /EBTTaphole下部爐壁 Walllowerpart上部爐壁Wallupperpart熱點Hotspot爐底Bottom MgO,%≥80≥76≥74≥72≥72C,%≥10≥12&g

2024-04-07 電議/噸

電爐爐底干式搗打料

2024-04-07 電議/噸